性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) astm d638/iso 527470kg/cm²(mpa)[lb/in2]断裂伸长率 astm d638/iso 52720%拉伸模量 astm d638/iso 52723500kg/cm²(mpa)[lb/in2]拉伸屈服伸长率(延伸率) astm d638/iso 5272.7%拉伸断裂伸长率(延伸率) astm d638/iso 52720%弯曲模量(弯曲弹性率) astm d790/iso 17824000kg/cm²(mpa)[lb/in2]弯曲强度 astm d790/iso 178700kg/cm²(mpa)[lb/in2]洛氏硬度 astm d785r-103 izod 缺口冲击强度1/4" 23℃astm d256/iso 179250kg·cm/cm(j/m)ft·lb/in1/4" -30℃astm d256/iso 179100kg·cm/cm(j/m)ft·lb/in1/8" 23℃astm d256/iso 179-kg·cm/cm(j/m)ft·lb/in1/8" -30℃astm d256/iso 179-kg·cm/cm(j/m)ft·lb/incharpy冲击强度23℃ （缺口）astm d256/iso 17923kg·cm/cm(j/m)ft·lb/in-30℃（缺口）astm d256/iso 17923kg·cm/cm(j/m)ft·lb/in23℃（无缺口）astm d256/iso 179210kg·cm/cm(j/m)ft·lb/in-30℃（无缺口）astm d256/iso 179110kg·cm/cm(j/m)ft·lb/in物性性能比重（密度） astm d792/iso 11831.04 成型收缩率 astm d9550.3-0.6%熔融指数（流动系数）200℃/5kgastm d1238/iso 11331.6g/10min220℃/10kgastm d1238/iso 113320g/10min吸水率 23℃/24h astm d570/iso 620.3%热性能热变形温度退火astm d648/iso 7599℃（℉）未退火astm d648/iso 75-℃（℉）维卡软化点 astm d1525/iso r30697℃（℉）熔点 --℃（℉）燃烧性（率） ul94hb 线性膨胀系数 astm d696/iso 113598-11mm/mm.℃加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 mpa保压压力 mpa背压 mpa螺杆转速 rpm其他备注 颜色 特性搞冲击、耐热。用途通信和电器产品。
大连鼎利化工有限公司
13898402440
中国 大连